Business Type:
Manufacturer/Factory
Business Range:
Calcined Alumina Powder, Alumina Ceramic Wear-resistance Product, Alumina Spray Dried ..
Establishment:
2006
R&D Capacity:
OEM
Terms of Payment:
LC, T/T, PayPal, WesternUnion
Main Markets:
South America, Europe, Southeast Asia, Middle East
OEM/ODM Service
Sample Available

Calcined Alumina, Corundum, Advanced Ceramics manufacturer / supplier in China, offering Calcined Alumina Powder for Refractory Castable, High Temperature Rotary Kiln Calcined Alumina Powder for Industrial Use, Spray Dried Alumina Powder for Industrial Ceramics and so on.

1
    YRS
General Supplier
Supplier Homepage Tools & Hardware Abrasive & Grinding Grinding Ball China Yttria Stabilized Zirconia Grinding Media

China Yttria Stabilized Zirconia Grinding Media

Get Latest Price
Min. Order / Reference FOB Price
1 Ton US $20600.00/ Ton
Local Area: Jian, Jiangxi, China
R&D Capacity: OEM, ODM, Other
Payment Terms: LC, T/T, PayPal, WesternUnion
Material: Zirconia
Content: >90%
Usage: Grind

Product Description
This is Y-TZP yttria stabilized zirconia grinding media, which is made of top quality zirconia powder, suitable for any kinds of mills such as ball mill, sand mill, attritor mill and vibratory mill.

Applications
Electronics Industry: Piezoelectric ceramics, inductance materials, capacitors ceramics, semiconductor ceramics, etc..
Battery Industry: Lithium iron phosphate, cobalt acid lithium materials, etc..
Chemical Industry: Paint, materials, printing ink, pigments, etc..
Ceramic Industry: Refractory materials, glaze materials, silicic acid zirconia, structural ceramics, etc..
Other Industry: Food, Medicine, Cosmetics

Features
1. Glossy satin smooth surface
2. Excellent tanacity & impact-resistance, making the beads keep fine in high rotation speed
3. Low friction coefficient makes lower abrasion to the equipment.
4. Y-TZP grinding media is over 30-50 times longer life than glass beads
5. Y-TZP grinding media is 5 times longer life than zirconium silicate beads.
6. Higher density than other grinding media
7. Y-TZP's grinding efficiency is 6-8 times than glass beads, 2-3 times than zirconium silicate beads.
Specifications


Composition (Wt%)
94.8+0.2% ZrO2,
5.2+0.2% Y2O3
Specific density (g/cm3)
≥6.0
Hardness HV (Gpa)
>12
Bending Strength (Mpa)
1150
Fracture toughness (Mpa·m1/2)
>9
Grain size (µm)
≤0.5
Elastic modulus (Gpa)
200
Thermal conductivity (W/m.k)
3 (20-400°C_
Coefficient of thermal expansion (10-6K-1)
9.6 (20-400°C)